4136.01GENERAL REQUIREMENTS
Use the type of joint fillers and sealers required in the contract documents.
4136.02CONTRACTION JOINT SEALERS AND SEALS
Meet the following requirements: A.
B.
Poured Joint Sealer. Approved sources for poured joint sealers are listed in Materials I.M. 436.01, Appendix A. 1.
Hot poured: Use sealers composed of petropolymers supplied in solid form and meeting the requirements of ASTM D 6690, Type IV.
2.
Cold applied: Use sealers that meet the requirements of ASTM D 5893.
Backer Rod. Approved backer rod sources are listed in Materials I.M. 436.04, Appendix A and B. If used in conjunction with joint sealers, obtain the Engineer's approval for composition. Use backer rod meeting the following requirements: 1.
When used with hot poured sealers, is capable of withstanding, without damage, the high temperatures inherent to the sealers.
2.
Has a maximum of 5% absorption when immersed in water for 24 hours with the ends sealed.
Joint Fillers, Sealers, and Seals
C.
4136.03
3.
Is of a size that compression is required for installation in the joint, so that it maintains its position during the sealing operation.
4.
Is dry and kept dry during installation.
5.
Is inspected and accepted according to Materials I.M. 436.04.
Preformed Elastomeric Joint Seal. Apply AASHTO M 220, including requirements for lubricant adhesive. Obtain Engineer's approval for the dimensions and shape.
4136.03EXPANSION JOINT FILLERS AND SEALS
Fill expansion joints with one of the following material types. When the type is not specified, use resilient filler. A.
B.
C.
Resilient Filler. 1.
Meet requirements of AASHTO M 213.
2.
Furnish in strips of dimensions shown in the contract documents.
3.
When the self expanding type is specifically required, use material meeting the requirements of AASHTO M 153, Type III. Use an accompanying sealer that meets the requirements of Article 4136.02, A.
4.
Approved resilient filler sources are listed in Materials I.M. 436.03, Appendix A.
5.
The Engineer may approve other resilient fillers.
Flexible Foam Expansion Joint Filler. 1.
Use the size designated in the contract documents.
2.
Ensure material is resistant to petroleum derivatives.
3.
Comply with the requirements of ASTM D 1752, Sections 5.1 to 5.4, with Section 5.3 modified to 10 psi minimum and 25 psi maximum when tested in accordance with AASHTO T 42.
4.
Approved sources for flexible foam expansion joint fillers are listed in Materials I.M. 436.05, Appendix A.
5.
Use sealer that meets the requirements of Article 4136.02, A.
Tire Buffings Expansion Joint Filler. When designated in the contract documents, use tire buffings to fill expansion joints. Comply with the following: 1.
Use buffings from the tire retreading industry. Approved sources for tire buffings for expansion joints are listed in Materials I.M. 436.06, Appendix A.
4136.03
D.
Joint Fillers, Sealers, and Seals
2.
Ensure tire buffings are clean, dry, and without any contamination.
3.
Place loose and strike off level.
4.
Remove compacted material and replace with loose material.
5.
Use sealer that meets the requirements of Article 4136.02, A. Approved sources for sealers are listed in Materials I.M. 436.01, Appendix A.
Elastomeric Joint Seals. 1.
Use elastomeric joint seals of the size designated in the contract documents and of a shape approved by the Engineer. Approved sources for elastomeric joint seals are listed in Materials I.M. 436.02, Appendix A. For the seal and the lubricant adhesive, meet the requirements of AASHTO M 220.
2.
Seals with splices will be acceptable only when splices are made using factory type methods the Engineer approves. Comply with the following: • Do not locate splices within 1 foot of a sharp bend, when placed in final position, and • Do not use more than one splice per finished piece.
Silicone Pre-Coated Surface. 1.
Furnish an expansion joint system comprised of the following three components:
polymer and factory coated with highway-grade, low modulus, fuel resistant silicone.
2.
Use an impregnation agent having proven non-migratory characteristics. The highway grade, low modulus, fuel resistant silicone facing shall be factory applied to the impregnated foam when the foam is at a width greater than the maximum working joint opening and once cured and compressed will form a bellows. The self-expanding foam sealant system shall have a depth as recommended by the manufacturer.
3.
Furnish material capable of movements of +/-50% (100% total) of nominal material size.
4.
Approved sources of sealant systems are listed in Materials I.M. 436.07, Appendix A