708.01 804 708 PAINT
708.01 Inorganic Zinc Silicate Primer Paint. Provide inorganic zinc silicate
primer paint conforming to AASHTO M 300, Type I, and the following modification: 5.1 A green colorant approximately No. 34159 of FS 595C. Follow the submittal requirements of Supplement 1084 to obtain approval of materials conforming to this specification. Once the Director approves the paint, the Department will not require further performance testing by the m anufacturer unless the formulation or manufacturing process has been changed, in which case the Department will require new certified test results . Furnish materials certified according to S 1084 and listed on the Department’s QPL.
708.02 OZEU Structural Steel Paint . This specification covers the
formulation and testing of a three -coat structural steel paint system consisting of an organic zinc prime coat, an epoxy intermediate coat, and a urethane finish coat (OZEU). Material requirements for the respective coats are as follows:
A.General. For each lot of all coatings, furnish a coated card (Drawdown card) that shows the color, gloss, and general appearance of the material covered by the lot. Use a minimum card size of 3 inches by 5 inches. The color must match the color card furnished for the Contract or order within visual limits determined by the Engineer. In case of disagreement, provide test data according to ASTM D 2244 showing a color difference of no greater tha n 2.0, ΔE* (CIE 1976 L*a*b*).
B.Organic Zinc Prime Coat. Provide an organic zinc prime coat consisting of a zinc dust filled, two or three -component epoxy polyamide, and selected additives as required. The coating shall also meet the following:
1.Phys ical Requirements.
a.Total solids, % by weight of paint, ASTM D 2369. 70 percent minimum.
b.Pigment, % by weight of total solids, ASTM D 2371. 83 percent minimum.
c.Total zinc dust, % by weight of pigment. ASTM D 521. 93 percent minimum.
d.Total zinc, % by weight of total solids (by calculation) ASTM D 521 . 77 percent minimum.
e.Total solids, % by volume, ASTM D 2697. 45 percent minimum.
f.Color. Greenish gray, approximating FS -595C -34159 , visual comparison. 708.02 805 g. Pot life. Follow the pai nt manufacturers recommendations for applying the coating within the pot life specified with no evidence of gellation. The coating will be in a free -flowing condition and easily sprayed.
2.Qualitative Requirements.
a.Mixing. Section 6.1, SSPC -Paint 20 using only a high shear (Jiffy) mixer.
b.Storage Life. Section 6.3, SSPC -Paint 20.
c.Mudcracking. Section 7.1, SSPC -Paint 20 .
3.Material Quality Assurance. Analysis for each component. Material Quality Assurance will conform to the requirements of S upplement 1084.
C.Epoxy Intermediate Coat. Provide a two -part epoxy intermediate coat composed of a base component and curing agent suitable for application over the zinc rich primer. The base component shall contain an epoxy resin together with color pi gments, mineral fillers, gellant, leveling agent, and volatile solvents. The curing agent component will contain a liquid polyamide resin and volatile solvent. The coating shall also meet the following:
1.Physical Requirements.
a.Color. White, meeting or exceeding, FS-595C -37875 according to ASTM E 1347.
b.Components. Two, mixed before application.
c.Volume solids, ASTM D 2697. 50 percent minimum.
d.Pot life. Follow the paint manufacturers recommendations for applying the coating within the pot life specified with no evidence of gellation. The coating will be in a free -flowing condition and easily sprayed.
e.Curing time.
1.Set-to-touch, ASTM D 1640. 4 hours, maximum at 77 F (25 C).
2.Dry-to-recoat, ASTM D 1640. 24 hours, maximum at 77 F (25 C).
f.Fineness of grind, ASTM D 1210. Hegman 3 minimum.
g.Volatile Organic Compounds (VOC), maximum, ASTM D 3960. 2.83 lb/gal(340 g/L), as applied.
2.Material Quality Assuran ce. Material Quality Assurance will conform to the requirements of Supplement 1084.
D.Urethane Finish Coat. Provide a two -component urethane finish coat composed of a polyester and/or acrylic aliphatic urethane and suitable for use as a 708.02 806 finish coat over the white epoxy polyamide intermediate coat. The coating shall also meet the following:
1.Physical Requirements.
a.Finish, Specular gloss, ASTM D 523. Use Fed. Std. 595C -16440 Gray: 70 % minimum after 3000 hours weathering resistance. Color change les s than 2.0 ΔE*, (C.I.E 1976 L*a*b*) ASTM D2244.
b.Volume solids, ASTM D 2697. 42 percent minimum.
c.Curing time, at 77 F (25 C) and 50% RH. Set-to-touch, ASTM D 1640: 30 minutes, minimum; 4 hours, maximum.
d.Pot life. Follow the paint manufacturers recommendations for applying the coating within the pot life specified with no evidence of gellation. The coating shall be in a free -flowing condition and easily sprayed
e.Volatile Organic Compounds (VOC), maximum, ASTM D 3960. 2.83 lb/gal(340 g/L), as applied.
f.Colors.
1.Specified.[2] Brown FS-595C, 10324 Green FS-595C, 14277 Blue FS-595C, 15526 [2] Contractor’s choice unless specified on plans
2.Elective. As specified on the plans.
g.Gloss requirements, ASTM D 523. Full gloss minimum 80% unless specified on the plans Semi -gloss 30 to 45% Lusterless (Matte) maximum 6%
2.Material Quality Assurance. Material Quality Assurance will conform to the requirements of Supplement 1084. Performance Requirements . Test the coating system, which consists of the organic zinc prime coat, the epoxy intermediate coat, and the urethane topcoat, prior to use. Prepare three pa nels for each of the specified tests according to ASTM D 609, except provide a minimum thickness of 1/8 inch (3 mm) and use ASTM A 36/A 36M hot rolled steel. Blast clean the surface to equal, as nearly as is practical, the stand ard Sa 2 1/2 of ASTM D 2200 (Steel Structures Painting Council SSPC -SP10 meets this requirement). Ensure that the surface has a nominal height of profile of 1 to 3.5 mils (25 to 88 m) verified by using appropriate replica tape. Coat and cure the panels according to the manufacturer’s printed instructions. Provide a dry film coating thickness for the system to be tested as follows: 708.02 807 Organic Zinc: 3.0 to 5.0 mils (75 to 125 m) Epoxy: 5.0 to 7.0 mils (125 to 175 m) Urethane: 2.0 to 4.0 mils (50 to 100 m) The coating system shall pass each of the following tests:
A.Fresh Water Resistance Test (ASTM D 870). Scribe the panels according to ASTM D 1654 to the depth of the base metal in the form of an “X” having at least 2-inch (50 mm) legs, and immerse p anels in fresh tap water at 75 5 F (25 3 C). After 30 days of immersion, examine the panels to verify that they show no rusting and that the coating shows no blistering, softening, or discoloration. Rate blistering according to ASTM D 714.
B.Salt Water Resistance Test (ASTM D 870). Scribe the panels as specified in “A” above, and immersed panels in a water solution of 5 percent sodium chloride at 75 5 F (25 3 C). After 7, 14, and 30 days of immersion, examine the panels to verify that they show no rusting and that the coating shows no blistering or softening. Rate blistering according to ASTM D 714. Replace the sodium chloride solution with a fresh solution after examination at 7 and 14 days.
C.Weathering Resistance Test. Test the panels according ASTM D 4587, Method D, using Ultra Violet A 340 bulbs. Place the panels on test at the beginning of a wet cycle. After 3000 hours of continuous exposure, examine the panels to verify that they show no rusting and that the coating shows no blis tering or loss of adhesion. Perform the 60 degree specular gloss measurements on the sprayed panels utilized for this test. Average the three initial measurements (one per panel) together. Also, average the three final measurements together.
D.Salt Fog Resistance Test. Scribe the panels as specified in “A” above, and test them according to ASTM B 117. After 3000 hours of continuous exposure, examine the coating to verify that it shows no loss of bond and that it shows no rusting or blistering beyond 1 /16 inch (2 mm) from the center of the scribe mark. Rate blistering according to ASTM D 714.
E.Adhesion Test, ASTM D 4541 Type IV. Test the panels according to the following:
1.Lightly sand the coating surface and aluminum dolly, and apply a quick set adhesive.
2.Allow adhesive to cure overnight.
3.Scribe the coating and adhesive around the dolly before testing.
4.Make a minimum of 4 trials to failure, and report the 4 trials. Ensure that each trial is greater than 400 pounds per square inch (2.8 MPa). Reject trial if fracture at the primer -blast interface occurs.
F.Pencil Hardness Test, ASTM D 3363 . Determine the hardness of an individual coat or the coating system by performing a Pencil Hardness Test according to ASTM D 3363. Meet or excee d scale of hardness HB for the coating.
Source: Ohio Construction and Material Specifications, 2019 Edition. Pages 0–0 of 928.